Bacterially induced crystal particle, thermal conductive material and method for manufacturing bacterially induced crystal particle

ABSTRACT

A bacterially induced crystal particle includes a composite shell. The composite shell layer may be hollow and has a thickness. The composite shell layer includes a biomaterial and a metallic material. The biomaterial is an organic substance including a cell wall or a cell membrane of a bacterium. The metallic material is oxides, sulfides, selenides, acid salt compounds of a transition metal, or any combination thereof. In other words, a bacterium itself is the template in the formation of a hollow sphere of transition-metal oxide mineral, transition-metal sulfide mineral, transition-metal selenide mineral, or transition-metal acid salt mineral. Accordingly, a material having low thermal conductivity can be provided.

CROSS-REFERENCE TO RELATED APPLICATION

This non-provisional application claims priority under 35 U.S.C. § 119(a) to Patent Application No. 105139567 in Taiwan, R.O.C. on Nov. 30, 2016, the entire contents of which are hereby incorporated by reference.

FIELD OF THE INVENTION

The instant disclosure relates to preparation techniques of nanomaterial, and more particular to a bacterially induced crystal particle, a thermal conductive material, and a method for manufacturing bacterially induced crystal particle.

BACKGROUND

Organisms like microorganisms, plants, and animals can become minerals in nature. A phenomenon called biomineralization means forming inorganic minerals in organisms. Cells of the organism are participated into the process of biomineralization, so that inorganic elements in the environments are selectively deposited on certain organic substances to form minerals. The microbial mineralization can be divided into two mineralization mechanisms, i.e., biologically induced mineralization (BIM) and biologically controlled mineralization (BCM).

The biologically induced mineralization of microorganisms can be further divided into two types, passive or active. The biologically induced mineralization in passive type is related to surface nucleation growth of the minerals resulted from nonspecific bonding between cations and anions in the nature. Regarding the biologically induced mineralization in active type, the metal ions combined on the surface of the microorganism may directly undergo a reduction-oxidative reaction and be transferred into minerals, or the side products in the metabolism of cells may react with ions in the environment to foul′ minerals on the cell surface.

The minerals are deposited on an organic matrix of a cell or on the surface or the interior of a vesicle of the cell. Accordingly, the organisms can control or confine the nucleation, growth, composition, size, and the position in the cell, of the mineral in some extent. This process is called biologically controlled mineralization. The mineral grains formed by biologically controlled mineralization usually have uniform structure, narrow size distribution, and specific and uniform types, uniform crystal habits, etc. In addition, during the biologically induced mineralization, the formation of the minerals can be induced when the ambient environment satisfies certain conditions. Conversely, during the biologically induced mineralization, all the environmental conditions in the cell (e.g., pH value, reduction-oxidation potential (Eh)) are controlled by the cell, therefore, the formation of the minerals can be hardly achieved.

SUMMARY OF THE INVENTION

In view of this, a bacterially induced crystal particle, a thermal conductive material, and a method for manufacturing bacterially induced crystal particle are provided.

In one embodiment, a bacterially induced crystal particle comprises a composite shell layer. The composite shell layer is hollow and has a thickness. The composite shell layer comprises a biomaterial and a metallic material. Wherein, the biomaterial is an organic substance comprising a cell wall or a cell membrane of a bacterium. The metallic material may be oxides, sulfides, selenides, or acid salt compounds of a transition metal, and the transition metal may be vanadium, niobium, tungsten, molybdenum, cobalt, zirconium, other alternative transition metal compounds, or any combination thereof. In other words, a bacterium itself is the template in the formation of a hollow sphere of transition-metal oxide mineral, transition-metal sulfide mineral, transition-metal selenide mineral, transition-metal acid salt mineral, other alternative transition metal compounds, or any combination thereof.

In one embodiment, a method for manufacturing bacterially induced crystal particle may comprise cultivating a bacterium in a cultivating medium for a period of time, so that the bacterium induces a raw metal material to undergo a reduction-oxidation reaction; isolating a wet powder material from the cultivating medium; and drying the wet powder material to obtain a powder material. Wherein, the cultivating medium may comprise a carbon source and a raw metal material, and the raw metal material is formed by a transition metal compound. The powder material may comprise the aforementioned bacterially induced crystal particle.

In one embodiment, a thermal conductive material may comprise the aforementioned bacterially induced crystal particle.

As above, the bacterially induced crystal particle, the thermal conductive material, and the method for manufacturing bacterially induced crystal particle, in accordance with one of the embodiments of the instant disclosure, are suitable for manufacturing a novel material, so that the material has a great low thermal conductivity. In addition, the method for manufacturing the bacterially induced crystal particle in accordance with one of the embodiments of the instant disclosure is easy, low cost, and can be directly applied in mass production.

BRIEF DESCRIPTION OF THE DRAWINGS

The instant disclosure will become more fully understood from the detailed description given herein below for illustration only, and thus not limitative of the instant disclosure, wherein:

FIG. 1 illustrates a schematic sectional view of a bacterially induced crystal particle of one embodiment of the instant disclosure;

FIG. 2 illustrates a perspective view of the bacterially induced crystal particle of one embodiment of the instant disclosure;

FIG. 3 illustrates a perspective view of the bacterially induced crystal particle of another embodiment of the instant disclosure;

FIG. 4 illustrates a flowchart of a method for manufacturing bacterially induced crystal particle of one embodiment of the instant disclosure;

FIG. 5 illustrates a flowchart of the method for manufacturing bacterially induced crystal particle of another embodiment of the instant disclosure;

FIG. 6 illustrates a scanning electron microscope (SEM) graph of the bacterially induced crystal particle of one embodiment of the instant disclosure;

FIG. 7 illustrates an energy dispersive X-ray spectroscopy (EDS) graph of the bacterially induced crystal particle of one embodiment of the instant disclosure; and

FIG. 8 illustrates a Raman spectroscopy graph of the bacterially induced crystal particle of one embodiment of the instant disclosure.

DETAILED DESCRIPTION

Hereinafter, the terminology “weight percentage” means the weight percentage calculated by taking the number of moles of the carbon in the carbon source as a standard.

Please refer to FIG. 1. In some embodiments, the bacterially induced crystal particle 10 may comprise a composite shell layer 100. The interior of the composite shell layer 100 is hollow, and the composite shell layer 100 comprises a biomaterial and a metallic material. The biomaterial may be formed by an organic substance, and the organic substance comprises a cell wall or a cell membrane of a bacterium. For example, the organic substance may only have a cell wall or a cell membrane of a bacterium as well as a small amount of other carbon-containing organics. The weight percentage of the biomaterial may be in a range of 5 to 80% over the composite shell layer, and the weight percentage of the biomaterial over the composite shell layer is greater than the weight percentage of the metallic material over the composite shell layer. The metallic material may be oxides, sulfides, selenides, acid salt compounds of a transition metal, or any combination thereof. In some embodiments, the metallic material may be oxides, sulfides, or selenides of the transition metal. In addition, the weight percentage of the transition metal element of the metallic material may be in the range from 3 to 75% over the composite shell layer.

In some embodiments, the biomaterial may be formed by an organic substance comprising a cell wall or a cell membrane of a Gram-negative bacterium. For example, the biomaterial may be formed by an organic substance, and the organic substance is a cell wall or a cell membrane of a Shewanella sp., a Pantoea sp., a Pseudomonas aeruginosa, or a Bacillus subtilis, embodiments are not limited thereto. In some embodiments, the metallic material may be oxides, sulfides, selenides, or acid salt compounds of a transition metal, and the transition metal may be vanadium, niobium, tungsten, molybdenum, cobalt, zirconium, other alternative transition metal compounds, or any combination thereof. The metallic material excludes from copper compounds and zinc compounds. For example, the metallic material may be a salt compound of vanadic acid, niobic acid, tungstic acid, or molybdenic acid.

In some embodiments, the biomaterial and the metallic material may be collocated properly according to application requirements and material property consideration. For example, in the case that the biomaterial is formed by an organic substance comprising a cell wall or a cell membrane of Shewanella sp., the metallic material may be a salt compound of tungstic acid or molybdenic acid. In the case that the biomaterial is formed by an organic substance comprising a cell wall or a cell membrane of Pantoea sp., the metallic material may be formed by a salt compound of molybdenic acid, tungstic acid, or vanadic acid.

In some embodiments, the interior of the composite shell layer 100 is hollow, and the composite shell layer 100 has a certain thickness. The “thickness” means a distance between any point on the inner surface of the composite shell layer 100 and any point on the outer surface of the composite shell layer 100 having a minimal value. In some embodiments, the thickness of the composite shell layer 100 may be in a range of 5 to 50 nm. In some embodiments, the thickness of the composite shell layer 100 may be in a range of 20 to 40 nm. Furthermore, the composite shell layer 100 may comprise two half shell layers, and the two half shell layers are dome-shaped.

Please refer to FIGS. 1 and 2, wherein FIG. 1 is a sectional view of the 1-1 line in FIG. 2. In some embodiments, the composite shell layer 100 may be sphere-shaped. The sphere-shaped composite shell layer 100 has a diameter. The “diameter” means the diameter of a concentric sphere between the inner surface and the outer surface of the sphere-shaped composite shell layer 100. In addition, a minimal distance between any point on the inner surface of the composite shell layer 100 and any point on the surface of the concentric sphere is substantially the same as a minimal distance between any point on the outer surface of the composite shell layer 100 and any point on the surface of the concentric sphere. In some embodiments, the diameter of the sphere-shaped composite shell layer 100 may be in a range of 0.2 to 2 μm. In some embodiments, the diameter of the sphere-shaped composite shell layer 100 may be 1 μm.

Please refer to FIGS. 1 and 3, wherein FIG. 1 is a sectional view of the 1-1 line in FIG. 3. In some embodiments, the composite shell layer 100 may be rod-shaped and has certain width and length. The rod-shaped composite shell layer 100 may comprise a middle portion 110 and two end portions 111 respectively connected to two ends of the middle portion 110. Wherein, the end portions 111 may be dome-shaped. Specifically, inner peripheries and outer peripheries of the two end portions 111 are respectively connected to inner peripheries and outer peripheries of the two ends of the middle portion 110. For each of the end portions 111, regarding the sectional plane having a maximal area, the “width” means a maximal distance between any two points on a line connected by middle points, and the middle points is at the center of a minimal distance between any point on the inner periphery of the sectional plane and any point on the outer periphery of the sectional plane; namely, the “width” is the width of the middle portion 110. For example, if the sectional plane of the maximal area of each of the end portions 111 is a circle, the width is the diameter of a concentric circle between the inner periphery of the sectional plane and the outer periphery of the sectional plane. In addition, a minimal distance between any point on the inner periphery of the end portion 111 and any point on the periphery of the concentric circle is substantially the same as that between any point on the outer periphery of the end portion 111 and any point on the periphery of the concentric circle. In some embodiments, the thickness of each of the end portions 111 is not less than 1/73 of the width of the composite shell layer 100, and the thickness of the middle portion 110 is not less than 1/37 of the width of the composite shell layer 100. In some embodiments, the width of the rod-shaped composite shell layer 100 may be in a range of 0.2 to 2 μm. In some embodiments, the width of the rod-shaped composite shell layer 100 may be 1 μm. In addition, the “length” of the rod-shaped composite shell layer 100 means a maximal distance between a middle point of the top end portion 111 and a middle point of the bottom end portion 111, the middle point of the top end portion 111 is at the center between a minimal distance between a top point of the outer surface of the top end portion 111 and a top point of the inner surface of the top end portion 111, and the middle point of the bottom end portion 111 is at the center between a minimal distance between a top point of the outer surface of the bottom end portion 111 and a top point of the inner surface of the bottom end portion 111. In some embodiments, the length of the rod-shaped composite shell layer 100 may be in a range of 1 to 10 μm.

Please refer to FIG. 4. In some embodiments, the method for manufacturing bacterially induced crystal particle may comprise following steps. Firstly, cultivating a bacterium in a cultivating medium for a period of time (S10). Wherein, the cultivating medium may comprise a carbon source and a raw metal material. During the cultivation, the bacterium will induce the raw metal material to undergo a reduction-oxidation reaction. And then, isolating a wet powder material from the cultivating medium (S20). Last, drying the wet powder material to obtain a powder material (S30). The powder material may be in a dispersive powder form or in an aggregation bulk form. Wherein, the powder material may comprise the aforementioned bacterially induced crystal particle 10. Furthermore, in some embodiments of the step S20, bubbles are formed on an upper layer of the cultivating medium, and a suspension is isolated from the bubbles to obtain the wet powder material.

In some embodiments, the bacterium may be a Gram-negative bacterium, e.g., Shewanella sp., Pantoea sp., Pseudomonas aeruginosa, Bacillus subtilis, other alternative Gram-negative bacteria, or any combination thereof. In one embodiment, the bacterium may be Shewanella sp., Pantoea sp., Pseudomonas aeruginosa, or Bacillus subtilis. The bacterium used in the cultivating step is the source of the biomaterial of the composite shell layer of the bacterially induced crystal particle. In some embodiments, the raw metal material may be transition metal compounds, e.g., acid salt compounds of the transition metals or oxygen-contained compounds of the transition metals. For example, the raw metal material may be salt compounds of vanadic acid, niobic acid, tungstic acid, or molybdenic acid, salt compounds of other transition metals, or any combination thereof. The raw metal material excludes from copper compounds and zinc compounds. The raw metal material may be the source of the metallic material of the composite shell layer of the bacterially induced crystal particle. For example, the metallic material of the composite shell layer may be formed by the raw metal material itself or a product from a reduction-oxidation reaction of the raw metal material.

In some embodiments, proper bacterium and raw metal material may be selected to obtain a desired powder material according to production requirements. For example, the bacterium in the cultivating medium may be Shewanella sp., and the raw metal material may be salt compounds of tungstic acid or molybdenic acid. In another example, the bacterium in the cultivating medium may be Pantoea sp., and the raw metal material may be salt compounds of molybdenic acid, tungstic acid, or vanadic acid. Furthermore, in some embodiments, the concentration of the raw metal material and the concentration of the carbon source in the cultivating medium may be respectively in a range of 0.01 to 0.2 M (molar concentration). In one embodiment, the concentration of the raw metal material in the cultivating medium may be in a range of 0.1 to 0.2 M.

In some embodiments, the “carbon source” means any substance having carbohydrate compounds as its major ingredient. The substance can provide energy for bacteria breeding and growth, and the substance can be served as a source of the essential carbon ingredient for bacterium synthesis. Any inorganic or organic carbon-containing compound capable of being utilized by microorganisms may be a carbon source, e.g., carbon dioxide, carbonates, saccharides or saccharide derivatives, alcohols, organic acids, lipids, hydrocarbons, aromatic compounds. For example, the carbon source may be glucose, sucrose, starch, fructose, lactose, lactates, formates, pyruvates, and/or amino acids. In some embodiments, the concentration of the carbon source in the cultivating medium may be in a range of 0.01 to 0.2 M. Furthermore, in some embodiments, the cultivating medium may be prepared by any proper commercial cultivating medium recipes, e.g., a Luria Broth (LB) medium, an M9 medium, other alternative cultivating medium, or any combination thereof.

Temperature has effect on bacterium growth. Therefore, the bacterium is cultivated under a proper temperature which is suitable for the growth of the bacterium. In one embodiment of the step S10, the bacterium is cultivated in the cultivating medium under an oxygen atmosphere at 37 degree Celsius. Cultivation time has effect on production of bacteria. Once the cultivation time is too short, the production of the bacteria will be insufficient, and the yield of the bacterially induced crystal particle is poor. In one embodiment of the step S10, the bacterium is placed in the cultivating medium and cultivated for at least three days. In another embodiment, the bacterium may be cultivated for 3 to 5 days.

In some embodiments, the step S20 further comprises centrifuging the cultivating medium or applying other alternative means to isolate a precipitate from the cultivating medium. In some embodiments, after the precipitate is isolated from the cultivating medium, an oscillation procedure with high frequency, e.g., ultrasonication, is further applied to the precipitate to break the precipitate. In addition, in some embodiments, the precipitate may be washed by a solvent, and the washing may be one time or more than two times. Common solvents, e.g., water, ethanol, other alternative solvents, or any combination thereof, may be applied to wash the precipitate. For example, RO water, deionized water, or ethanol may be applied to wash the precipitate. Please refer to FIG. 5, in some embodiments, after the step S10, centrifuging the cultivating medium to form a precipitate (i.e., the wet powder material) (S200). And then, breaking the precipitate to form a crude powder material (S300), and washing the crude powder material by a solvent in at least one time (S400). Last, air drying or heating the precipitate under a proper temperature to dry the precipitate (S500), so that the solvent in the precipitate is removed and the powder material is obtained. Furthermore, in some embodiments, the density of the powder material is 420 kg/m².

In some embodiments, the bacterially induced crystal particle may be utilized in preparing materials with great physical and/or chemical properties, e.g., in preparing a thermal conductive material. In some embodiments, the thermal conductive material may comprise the aforementioned bacterially induced crystal particle. In another embodiment, the thermal conductive material is formed by the aforementioned bacterially induced crystal particles. In some embodiments, the thermal conductivity of the bacterially induced crystal particle may be in a range of 0.027 to 0.15 Watt/meter*Kelvin (W/mK). In some embodiments, the thermal conductivity of the bacterially induced crystal particle may be 0.058 W/mK.

In some embodiments, the ingredients of the cultivating medium or the amount of the raw metal material may be adjusted to allow the composite shell layer of the bacterially induced crystal particle having two half shell layer in dome-shaped. For example, comparing with a normal cultivating procedure, the saccharide (i.e., the carbon source) in the cultivating medium or the concentration of the raw metal material may be adjusted, so that the bacterium suffers a stress response and the appearance of the bacterium is changed. In some embodiments, using the raw metal material in high concentration (e.g., 0.1 to 0.2 M), may facilitate the stress response to make the appearance of the bacterium in the cultivating medium change. In some embodiments, the change of the appearance of the bacterium may cause the cell wall of the bacterium forms a structure with two dome-shaped portions, e.g., a sphere or a rod with two dome-shaped portions. Accordingly, the composite shell layer may have two half shell layers in dome-shaped. In some embodiments, the composite shell layer is sphere-shaped or rod-shaped with two half shell layers in dome-shaped.

In some embodiments, the composite shell layer of the bacterially induced crystal particle may further undergo an oxidation reaction, a sulfurization reaction, or a selenization reaction. For example, the metallic material may be reacted with oxygen in the environment to font′ an oxide of a transition metal under a high temperature (e.g., 300 to 1000 degree Celsius) and/or an oxygen-rich environment, and most of the composite shell layer is formed by the metallic material which is the transition metal oxide. Herein, the transition metal oxide is only formed by a transition metal element and oxygen atom(s), and excludes from transition metal carboxylate or compounds having oxygen atom(s). In another embodiment, for example, the composite shell layer treated by oxidation reaction may undergo a sulfurization by mechanical ablation or chemical vapor deposition, so that the oxygen atoms in the transition metal oxide of the metallic material can be replaced by sulfur atoms in the replacement reaction. In this embodiment, most of the composite shell layer is formed by the metallic material which is the transition metal sulfide. Similarly, the composite shell layer treated by oxidation reaction may undergo a selenization by mechanical ablation or chemical vapor deposition, so that the oxygen atoms in the transition metal oxide of the metallic material can be replaced by selenium atoms in the replacement reaction, and in this embodiment, most of the composite shell layer is fotined by the metallic material which is the transition metal selenide. Furthermore, the changes of the characters of the composite shell layer before and after the oxidation, the sulfurization, and the selenization can be measured by Raman spectroscopy, photoluminescence spectroscopy, electron microscope, etc. For example, by utilizing photoluminescence spectroscopy to measure the composite shell layer, the energy gap of the metallic material of the composite shell layer is detected to be in a range of 1.2 to 1.8 eV (electron volt).

In some embodiments, the powder material may be placed in a reactor, and the powder material is heated with oxygen, sulfur vapor (e.g., hydrogen sulfide), or selenium vapor (e.g., hydrogen selenide), under a temperature in a range of 300 to 1000 degree Celsius or under a proper temperature, for a period of time. That is, the powered material is sintered. Accordingly, the composite shell layer of the bacterially induced crystal particle in the powder material undergoes an oxidation reaction, a sulfurization reaction, or a selenization reaction, so that most of the metallic material of the composite shell layer is a transition metal oxide, a transition metal sulfide, or a transition metal selenide. In some embodiments, after the composite shell layer undergoes the oxidation, the sulfurization, or the selenization, the weight percentage of the biomaterial is in a range of 1 to 5% over the composite shell layer, and the weight percentage of the metallic material over the composite shell layer is greater than the weight percentage of the biomaterial over the composite shell layer.

For example, the bacterially induced crystal particle may be manufactured by following steps. Firstly, Shewanella sp. is obtained from white shrimp (scientific name: litopenaeus vannamei). And then, under a 37 degree Celsius environment, the Shewanella sp. is cultivated in a cultivating medium (e.g. an LB cultivating medium or an M9 cultivating medium) for 16 hours. Next, about 0.01 to 0.2 M carbon source and about 0.01 to 0.2 M tungstate are added into the cultivating medium, and the Shewanella sp. is further cultivated for 3 to 5 days. After the cultivation process, the cultivating medium is centrifuged to remove the supernatant and to obtain the precipitate. And then, the precipitate is ultrasonicated so as to break the precipitate. Next, the broken precipitate (i.e., the crude powder material) is washed by deionized water for several times, and the broken precipitate is suspended in ethanol. Last, the suspension is dried under 40 degree Celsius to obtain the powder material. The powder material comprises the bacterially induced crystal particle and is powder and inviscid.

The powder material is compressed to tablet powder material by a 10 MPa pressure for subsequent property measurements. Firstly, the volume and the weight of the tablet powder material are measured, and the density is calculated to be 420 kg/m². Under atmospheric environment, the tablet powder material is measured by a field emission scanning electron microscope (FESEM) (model: JEOL JSM-6500F) for SEM image analysis and energy-dispersive X-ray spectroscopy (EDS). In addition, the thermal conductive properties of the tablet powder material are analyzed by a Tci thermal conductivity analyzer with modified transition plane source (manufactured by C-Therm Technologies Ltd.). Furthermore, the main ingredients of the tablet powder material are analyzed by a Raman spectrometer.

Please refer to FIG. 6. From the SEM image, bacterially induced crystal particles with composite shell layers can be seen in the powder material. Each of the composite shell layers is sphere-shaped and has a smooth surface. The diameter of each of the composite shell layers is about 1 μm, and the thickness of each of the composite shell layers is about 20 to 40 nm. Therefore, air occupies most of the spaces in the composite shell layers. In addition, the composite shell layers can bear such pressure and does not break or suffer any structural damages even if the powder material is compressed to form tablet powder material. From the analyzing result of the thermal conductivity properties of the tablet powder material, the thermal conductivity of the bacterially induced crystal particle is 0.058 W/mK, the thermal effusivity of the bacterially induced crystal particle is 124.22 WS^(1/2)/m²K, and the thermal diffusivity of the bacterially induced crystal particle is 2.54 m²/s. Because most of the space in the composite shell layer is occupied by air, the thermal conductivity of the bacterially induced crystal particle is extremely low, only about two times of that of the stationary air.

Please refer to FIG. 7. The EDS shows that elements comprising carbon, oxygen, tungsten, and other metals like sodium are detected in the composite shell layer of the bacterially induced crystal particle. As shown, the metallic material of the composite shell layer may comprise sodium tungstate. Furthermore, the crystalline structure of tungsten oxides, like tungsten trioxide or tungsten dioxide is mainly in a three dimensional structure, while the crystalline structure of tungstate is mainly in a two dimensional structure. Therefore, the major ingredient of the metallic material may comprise sodium tungstate and other tungstate. Please refer to FIG. 8, the Raman spectroscopy shows that two major peaks are located at 980 cm⁻¹ and 737 cm⁻¹, respectively. The peak at 980 cm⁻¹ is mainly attributed by magnesium tungstate, and the peak at 737 cm⁻¹ is mainly attributed by sodium tungstate. Therefore, from FIGS. 7 and 8, the metal material mainly comprises magnesium tungstate and sodium tungstate.

According to embodiments of the instant disclosure, the thickness of the composite shell layer of the bacterially induced crystal particle is in nanometer scale, and the width is in micrometer scale. Therefore, it is inferred that the material occupation ratio of the bacterially induced crystal particle is low. Next, as compared with the sodium tungstate having a density of 4179 kg/m³, the density of the bacterially induced crystal particle is about 1/10 of that of sodium tungstate. Therefore, it is inferred that the volume ratio of the metallic material over the bacterially induced crystal particle is about 1/10. In general, when a material has low material occupation ratio, the material also has a low thermal conductivity. In addition, when the bacterially induced crystal particle may be deemed as the combination of two dome structures, the appearance of the bacterially induced crystal particle may be sphere-shaped or may be ellipsoid-shaped like rugby. In another embodiment, the bacterially induced crystal particle may be a rod having two dome-shaped end portions. because tungstate may be applied as the raw material for stone, the bacterially induced crystal particle of the embodiments of the instant disclosure may be deemed as a stone having dome structures. For a stone-made arch having a dome structure vault, the thickness of the vault may be less than the thickness of the wall of the arch. In addition, the thickness of the vault may be greater than or equal to 1/73 of the width of the arch, and the thickness of the wall of the arch may be greater than or equal to 1/37 of the width of the arch. If the thickness of the wall of the arch is too thin, the arch structure would be fragile and the connection between the vault and the wall would be prone to break. Likewise, according to embodiments of the instant disclosure, in the case that the composite shell layer of the bacterially induced crystal particle is rod shaped, if the thickness of the middle portion is less than 1/37 of the width of the composite shell layer, the connection between the middle portion and the end portion may be fragile and prone to break.

As above, the bacterially induced crystal particle, the thermal conductive material, and the method for manufacturing bacterially induced crystal particle, in accordance with one of the embodiments of the instant disclosure, are suitable for manufacturing a novel material. By utilizing a principle of microorganism mineralization, bacterially induced crystal particle with low material occupation ratio and great thermal conductivity can be obtained. Moreover, the method for manufacturing the bacterially induced crystal particle is easy, low cost, and prone to have mass production. In addition, the dome structure of the bacterially induced crystal particle can be maintained after being compressed by a 10 MPa pressure. Therefore, the bacterially induced crystal particle may be applied in mass production of a novel thermal conductive material, so that the thermal conductive material can have low thermal conductivity, great pressure resistance, and reduced manufacturing cost. Furthermore, the bacterially induced crystal particle, in accordance with one of the embodiments of the instant disclosure may be widely applied in developing products based on low thermal conductivity nanomaterial.

While the instant disclosure has been described by the way of example and in terms of the preferred embodiments, it is to be understood that the invention need not be limited to the disclosed embodiments. On the contrary, it is intended to cover various modifications and similar arrangements included within the spirit and scope of the appended claims, the scope of which should be accorded the broadest interpretation so as to encompass all such modifications and similar structures. 

What is claimed is:
 1. A bacterially induced crystal particle, comprising: a composite shell layer, being hollow and having a thickness, wherein the composite shell layer comprises: a biomaterial, wherein the biomaterial is an organic substance comprising a cell wall or a cell membrane of a bacterium; and a metallic material, wherein the metallic material is oxides, sulfides, selenides, acid salt compounds of a transition metal or any combination thereof.
 2. The bacterially induced crystal particle according to claim 1, wherein the weight percentage of the biomaterial is in a range of 5 to 80% over the composite shell layer.
 3. The bacterially induced crystal particle according to claim 2, wherein the weight percentage of the biomaterial over the composite shell layer is greater than the weight percentage of the metallic material over the composite shell layer.
 4. The bacterially induced crystal particle according to claim 1, wherein the bacterium is a Gram-negative bacterium.
 5. The bacterially induced crystal particle according to claim 4, wherein the Gram-negative bacterium is Shewanella sp., Pantoea sp., Pseudomonas aeruginosa, Bacillus subtilis, or any combination thereof.
 6. The bacterially induced crystal particle according to claim 1, wherein the weight percentage of the metallic material over the composite shell layer is greater than the weight percentage of the biomaterial over the composite shell layer after the bacterially induced crystal particle is sintered.
 7. The bacterially induced crystal particle according to claim 6, wherein the weight percentage of the biomaterial is in a range of 1 to 5% over the composite shell layer.
 8. The bacterially induced crystal particle according to claim 1, wherein the transition metal is vanadium, niobium, tungsten, molybdenum, cobalt, nickel, or zirconium.
 9. The bacterially induced crystal particle according to claim 1, wherein the acid salt compound is a salt compound of vanadium acid, niobic acid, tungstic acid, or molybdenic acid.
 10. The bacterially induced crystal particle according to claim 1, wherein the biomaterial is a cell wall or a cell membrane of Shewanella sp., and the metallic material is a salt compound of tungstic acid or molybdenic acid.
 11. The bacterially induced crystal particle according to claim 1, wherein the biomaterial is a cell wall or a cell membrane of Pantoea sp., and the metallic material is a salt compound of molybdenic acid, tungstic acid, or vanadic acid.
 12. The bacterially induced crystal particle according to claim 1, wherein the composite shell layer comprises two half shell layers, the two half shell layers are dome-shaped.
 13. The bacterially induced crystal particle according to claim 1, wherein the composite shell layer is sphere-shaped.
 14. The bacterially induced crystal particle according to claim 13, wherein a diameter of the composite shell layer is in a range of 0.2 to 2 μm.
 15. The bacterially induced crystal particle according to claim 1, wherein the composite shell layer is rod-shaped and has a width and a length, and the composite shell layer comprises: a middle portion; and two end portions, wherein the two end portions are dome-shaped and respectively connected to two ends of the middle portion; wherein a thickness of each of the end portions is not less than 1/73 of the width of the composite shell layer, and a thickness of the middle portion is not less than 1/37 of the width of the composite shell layer.
 16. The bacterially induced crystal particle according to claim 15, wherein the width of the composite shell layer is in a range of 0.2 to 2 μm.
 17. The bacterially induced crystal particle according to claim 15, wherein the length of the composite shell layer is in a range of 1 to 10 μm.
 18. The bacterially induced crystal particle according to claim 1, wherein the thickness of the composite shell layer is in a range of 5 to 50 nm.
 19. A thermal conductive material, comprising: a bacterially induced crystal particle according to claim
 1. 20. The thermal conductive material according to claim 19, wherein the thermal conductivity of the bacterially induced crystal particle is in a range of 0.027 to 0.15 W/mK.
 21. A method for manufacturing bacterially induced crystal particle, comprising: cultivating a bacterium in a cultivating medium comprising a carbon source and a raw metal material for a period of time, so that the bacterium induces the raw metal material to undergo a reduction-oxidation reaction, wherein the raw metal material is formed by a transition metal compound; isolating a wet powder material from the cultivating medium; and drying the wet powder material to obtain a powder material, wherein the powder material comprises at least one bacterially induced crystal particle.
 22. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein after the step of cultivating the bacterium in the cultivating medium, further comprises: allowing an upper layer of the cultivating medium to form bubbles; and isolating a suspension from the bubbles to obtain the wet powder material.
 23. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein the bacterium is a Gram-negative bacterium.
 24. The method for manufacturing bacterially induced crystal particle according to claim 23, wherein the Gram-negative bacterium is Shewanella sp., Pantoea sp., Pseudomonas aeruginosa, Bacillus subtilis, or any combination thereof.
 25. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein the raw metal material is formed by an acid salt compound of the transition metal.
 26. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein the raw metal material is a salt compound of vanadic acid, niobic acid, tungstic acid, molybdenic acid, cobaltic acid, nickelic acid, zirconic acid, or any combination thereof.
 27. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein the bacterium is Shewanella sp., and the raw metal material is a salt compound of tungstic acid or molybdenic acid.
 28. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein the bacterium is Pantoea sp., and the raw metal material is a salt compound of molybdenic acid, tungstic acid, or vanadic acid.
 29. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein in the step of cultivating the bacterium in the cultivating medium, the bacterium suffers a stress response, so that a cell wall or a cell membrane of the bacterium forms two portions in dome-shaped, and the bacterially induced crystal particle is sphere shaped or rod shaped with two half shell layers in dome-shaped.
 30. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein a concentration of the raw metal material in the cultivating medium is in a range of 0.01 to 0.2 M.
 31. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein a density of the powder material is 420 kg/m³.
 32. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein the step of cultivating the bacterium in the cultivating medium comprises: cultivating the bacterium in the cultivating medium under an oxygen atmosphere at 37 degree Celsius for a period of time.
 33. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein the cultivating medium is an LB medium or an M9 medium.
 34. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein a cultivation time in the step of cultivating the bacterium in the cultivating medium is in a range of 3 to 5 days.
 35. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein a concentration of the carbon source in the cultivating medium is in a range of 0.01 to 0.2 M.
 36. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein the step of isolating the wet powder material from the cultivating medium comprises: centrifuging the cultivating medium to form a precipitate; and isolating the precipitate from the centrifuged cultivating medium to obtain the wet powder material.
 37. The method for manufacturing bacterially induced crystal particle according to claim 36, wherein after the step of isolating the precipitate from the centrifuged cultivating medium, further comprises: breaking the wet powder material to form a crude powder material.
 38. The method for manufacturing bacterially induced crystal particle according to claim 37, wherein the step of breaking the wet powder material comprises: ultrasonicating the wet powder material.
 39. The method for manufacturing bacterially induced crystal particle according to claim 37, wherein after the step of breaking the wet powder material, further comprises: washing the crude powder material by a solvent in at least one time.
 40. The method for manufacturing bacterially induced crystal particle according to claim 39, wherein the step of drying the wet powder material comprises: drying the crude powder material to obtain the powder material.
 41. The method for manufacturing bacterially induced crystal particle according to claim 21, wherein the bacterially induced crystal particle comprises a composite shell layer, the composite shell layer is hollow and has a thickness.
 42. The method for manufacturing bacterially induced crystal particle according to claim 41, wherein the composite shell layer comprises: a biomaterial, wherein the biomaterial is formed by an organic substance comprising a cell wall or a cell membrane of a bacterium; and a metallic material, wherein the metallic material is formed by oxides, sulfides, selenides, acid salt compounds of a transition metal, or any combination thereof.
 43. The method for manufacturing bacterially induced crystal particle according to claim 41, further comprising: heating the powder material in oxygen, so that the composite shell layer of the bacterially induced crystal particle undergoes an oxidization reaction to have the metallic material comprising an oxide of the transition metal.
 44. The method for manufacturing bacterially induced crystal particle according to claim 41, further comprising: heating the powder material in a sulfur vapor, so that the composite shell layer of the bacterially induced crystal particle undergoes a sulfurization reaction to have the metallic material comprising a sulfide of the transition metal.
 45. The method for manufacturing bacterially induced crystal particle according to claim 41, further comprising: heating the powder material in a selenium vapor, so that the composite shell layer of the bacterially induced crystal particle undergoes a selenization reaction to have the metallic material comprising a selenide of the transition metal. 